Preparation and Characteristics of an Environmentally Friendly Hyperbranched Flame-Retardant Polyurethane Hybrid Containing Nitrogen, Phosphorus, and Silicon

文化大學機構典藏 CCUR > 理工學院 > 工學院 > 化學工程與材料工程學系暨碩士班 > 期刊論文 > Item 987654321/44633

請使用永久網址來引用或連結此文件: https://irlib.pccu.edu.tw/handle/987654321/44633

題名:	Preparation and Characteristics of an Environmentally Friendly Hyperbranched Flame-Retardant Polyurethane Hybrid Containing Nitrogen, Phosphorus, and Silicon
作者:	Chen, CH (Chen, Chin-Hsing) Chiang, CL (Chiang, Chin-Lung)
貢獻者:	化學工程與材料工程學系暨奈米材料研究所
關鍵詞:	THERMOPLASTIC POLYURETHANE THERMAL-DECOMPOSITION BEHAVIOR DEGRADATION FOAMS
日期:	2019-04
上傳時間:	2019-06-25 11:42:34 (UTC+8)
摘要:	The NCO functional group of 3-isocyanatoproplytriethoxysilane (IPTS) and the OH functional group of 10-(2,5-dihydroxyphenyl)-10H-9-oxa-10-phospha-phenantbrene-10-oxide (DOPO-BQ) were used to conduct an addition reaction. Following completion of the reaction, triglycidyl isocyanurate (TGIC) was introduced to conduct a ring-opening reaction. Subsequently, a sol-gel method was used to initiate a hydrolysis-condensation reaction on TGIC-IPTS-DOPO-BQ to form a hyperbranched nitrogen-phosphorous-silicon (HBNPSi) flame retardant. This flame retardant was incorporated into a polyurethane (PU) matrix to prepare a hybrid material. Fourier-transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), limiting oxygen index (LOI), UV-VIS spectrophotometry, and Raman analysis were conducted to characterize the structure and analyze the transparency, thermal stability, flame retardancy, and residual char to understand the flame retardant mechanism of the prepared hybrid material. After the flame retardant was added, the maximum degradation rate decreased from -36 to -17 wt.%/min, the integral procedural decomposition temperature (IPDT) increased from 348 to 488 degrees C, and the char yield increased from 0.7 to 8.1 wt.%. The aforementioned results verified that the thermal stability of PU can be improved after adding HBNPSi. The LOI analysis indicated that the pristine PU was flammable because the LOI of pristine PU was only 19. When the content of added HBNPSi was 40%, the LOI value was 26; thus the PU hybrid became nonflammable.
關聯:	Polymers 2019, 11(4), 720
顯示於類別:	[化學工程與材料工程學系暨碩士班] 期刊論文