Wear behavior of nitrocarburized JIS SKD61 tool steel

文化大學機構典藏 CCUR > 理工學院 > 工學院 > 機械工程系暨機械工程學系數位機電研究所 > 期刊論文 > Item 987654321/2933

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://irlib.pccu.edu.tw/handle/987654321/2933

题名:	Wear behavior of nitrocarburized JIS SKD61 tool steel
作者:	Chiu L.H. Wu C.H. Chang H
贡献者:	機械系
关键词:	JIS SKD61 tool steel nitrocarburizing wear
日期:	2002
上传时间:	2009-12-04 14:53:30 (UTC+8)
摘要:	The surface wear characteristics of the nitrocarburized JIS SKD61 tool steel were investigated. The ferritic substrate (FS) JIS SKD61 tool steel as received was pretreated in quenching and tempering processes to obtain the tempered martensitic microstructure. Specimens were then nitrocarburized for 1, 3, and 5 h. The chemistry, microstructure, and hardness of the nitrocarburized coatings were analyzed. Wear behavior was examined on a block-on-roller wear tester under unlubricated conditions. The results have shown that white layers were predominantly composed of the E-phase iron nitrides dispersed with gamma'-phase, and a large amount of nitrogen and carbon trapped in the ferrite phase was observed in the diffusion layer for FS. The nitrocarburizing treatment increased the surface roughness, hardness and the friction coefficients of the specimens. Wear contact pressures and nitrocarburized holding time also affected the friction coefficients of the nitrocarburized specimens. In this study, both the FS and the tempered martensitic substrate (TMS) specimens treated with subsequent nitrocarburizing process have shown significant improvement of the wear resistance. Wear behaviors of the specimens nitrocarburized for 1, 3, and 5 h did not vary significantly. (C) 2002 Elsevier Science B.V. All rights reserved.
關聯:	WEAR Volume: 253 Issue: 7-8 Pages: 778-786
显示于类别:	[機械工程系暨機械工程學系數位機電研究所] 期刊論文