Fracture behaviors of PP/mPE thermoplastic vulcanizates via silane crosslinking

文化大學機構典藏 CCUR > 理工學院 > 工學院 > 化學工程與材料工程學系暨碩士班 > 期刊論文 > Item 987654321/2531

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://irlib.pccu.edu.tw/handle/987654321/2531

题名:	Fracture behaviors of PP/mPE thermoplastic vulcanizates via silane crosslinking
作者:	Lai, S. -M. Chen, W. -C. Hu, N. -H. Wang, D. S. -T.
贡献者:	化材系
关键词:	metallocene polyethylene (mPE) thermoplastic vulcanizate (TPV) silane crosslinking mechanical properties
日期:	2008
上传时间:	2009-11-06 11:24:16 (UTC+8)
摘要:	We prepared silane cured PP/metallocene polyethylene to form a thermoplastic vulcanizate. Metallocene polyethylenes (mPE) with two different levels of comonomer contents were grafted with various amounts of vinyltriethoxy silane. Thermal behaviors remained largely unchanged for PP, indicating a dominant effect of cured mPE domains on mechanical properties for the vulcanizates. Tensile strength decreased with increasing the levels of silane concentrations but leveled off at higher silane concentrations at all test temperatures. Tear strength generally decreased with reduced energy dissipation at higher degrees of cure. By relating tensile strength to tear strength, the corrected depth of flaw was ca. 85 +/- 8 mu m which was about twice higher than the natural flaw size of 40 +/- 20 mu m obtained from several different approaches for conventional elastomer, but comparable for other types of thermoplastic vulcanizates. The application of Rivlin and Thomas's theory for this newly developed TPV should be cautious due to its limitation. A further modification of previous theory for thermoplastic elastomers is necessary. The crack tip diameter (effective diameters of fracture zones) deduced from intrinsic energy density and tear strength gave a similar order in comparison with several materials.
關聯:	JOURNAL OF POLYMER ENGINEERING Volume: 28 Issue: 4 Pages: 203-223
显示于类别:	[化學工程與材料工程學系暨碩士班] 期刊論文