| 題名: | Effect of intercalant types on the properties of melt blended metallocene polyethylene/metallocene polyethylene-g-silane/clay nanocomposites |
| 作者: | Chen, WC (Chen, Wen-Chih)
Liu, JL (Liu, Jung-Liang)
Lai, SM (Lai, Sun-Mou)
Tang, SX (Tang, Shi-Xian)
Tai, HJ (Tai, Horng Jer)
Yang, CH (Yang, Chen-Hau)
Kao, HC (Kao, Hui Cheng) |
| 貢獻者: | Dept Chem Engn |
| 關鍵詞: | clay
clay types
compatibilizer
metallocene polyethylene
nanocomposite |
| 日期: | 2012-12 |
| 上傳時間: | 2013-02-18 15:26:59 (UTC+8) |
| 摘要: | Melt mixed metallocene-catalyzed polyethylene elastomer (mPE)/clay nanocomposites, using a functionalized polyolefin elastomer (mPE-g-silane) as a compatibilizer, with the addition of the commercial clay with different intercalant types (Cloisite 20A and 30B) were prepared to investigate the importance of interfacial interaction. Cloisite 30B gave a relatively higher polarity than Cloisite 20A, but smaller original d-spacing. According to X-ray diffraction (XRD) and transmission electron microscopy (TEM) results, Cloisite 20A-filled nanocomposites depicted fairly well-dispersed clay within the mPE matrix, except with higher clay content. By contrast, the clay agglomerates were evident for Cloisite 30B-filled cases. A continuous increase of gel content for Cloisite 20A-filled systems was observed, but only a limited variation for Cloisite 30B-filled systems was found. The roles of the polarity degree of the organically modified clay, original d-spacing, and the compatibilizer, were quite essential. Young's modulus of Cloisite 20A-filled samples increased with increasing clay content, from 23.8 +/- 1.3 MPa [0 parts per hundred resins (phr)] to 34.1 +/- 2.0 MPa (9 phr), whereas modulus of Cloisite 30B-filled samples did not show a significant variation. The tear strength of Cloisite 20A-filled nanocomposites increased up to two-fold with increasing clay content, reaching 9 phr. Only a slight increase in tear strength of Cloisite 30B-filled nanocomposites was observed. For the cutting strength, Cloisite 20A-filled cases also conferred higher values in comparison with Cloisite 30B-filled cases. |
| 關聯: | JOURNAL OF POLYMER ENGINEERING 卷: 32 期: 8-9 頁數: 475-485 |