    題名: The Unidirectional Glass Fiber Reinforced Furfuryl Alcohol for Pultrusion. II. Correlation of Processing Parameters for Optimizing the Process
    作者: Chen, CH (Chen, Chin-Hsing)
    Chen, IK (Chen, I-Ken)
    貢獻者: Dept Chem & Mat Engn
    關鍵詞: pultrusion;glass fiber
    furfuryl alcohol
    processing parameters
    composites
    日期: 2011-02-05
    上傳時間: 2013-01-25 10:15:34 (UTC+8)
    摘要: Unidirectional glass fiber reinforced furfuryl alcohol (FA) composites have been prepared by the pultrusion processes. The optimum processing parameters of the glass fiber reinforced FA composites by pultrusion has been studied. The effects of the optimum processing parameters on the properties (flexural strength, flexural modulus, notched Izod impact strength, glass transition temperature (T(g)), dynamic shear storage modulus (E'), shrinkage ratio, and roughness) investigated including die temperature, pulling rate, postcure temperature and time, and filler type and content. Results show that the pultruded composites possessed various optimum pulling rates at different die temperatures. On the basis of the DSC diagram, the swelling ratio and the mechanical properties of pultruded composites, the optimum die temperature can be determined. The mechanical properties and T(g) increase at a suitable postcure temperature and time. Furthermore, the properties which decrease due to the degradation of pultruded composites for a long postcure time will be discussed. The mechanical properties of pultruded composites reach a maximum value at various filler content corresponding to the talc and calcium carbonate, respectively, and then decreased. When the fillers are added to the pultruded glass fiber reinforced FA composites, the shrinkage ratio of composites become smaller, and the surface of composites became smooth. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 119: 1788-1796, 2011
    關聯: JOURNAL OF APPLIED POLYMER SCIENCE 卷: 119 期: 3 頁數: 1788-1796
    顯示於類別:[Department of Chemical & Materials Engineering] journal articles

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML359檢視/開啟


    檢視Licence

    在CCUR中所有的資料項目都受到原著作權保護.

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋