Title:	Phase transformation and mechanical behavior of TiFeCoNi alloy during annealing
Authors:	Tsau, CH (Tsau, Chun-Huei)
Contributors:	化材系
Date:	2009-02
Issue Date:	2011-12-09 11:15:23 (UTC+8)
Abstract:	Adding Ti to FeCoNi alloy modified its microstructure to a two-phased dendritic microstructure, improving its mechanical properties. The phases in the as-cast TiFeCoNi alloy were hard ordered HCP dendrites and soft ordered FCC-interdend rite matrix. Annealing at 1000 degrees C did not alter the HCP-dendrite structure, but decomposed the FCC-interdendritic matrix and reduced its degree of order. Experimental results indicate that the internal stress due to casting is released in the initial stage of annealing. Then, the phase transformation increases both the ultimate compressive strength and the plastic strain. The TiFeCoNi alloy that was annealed at 1000 degrees C for 24 h had excellent mechanical properties-a yield strength of 1.33 GPa, an ultimate compressive strength of 2.6 GPa and a plastic strain of 20%. (c) 2008 Elsevier B.V. All rights reserved.